We offer a wide range of materials that can cater to your specific needs. Below is list of materials along with their chemical composition, mechanical property values & density. Special grade materials are offered on-request.
Material>>> | SS 17-4PH | 42CrMo4 | 16Mo Cr5 | 100 Cr6 | SS 310 N | SS 304 | SS 316L | SS 420 W | 1010 | 4605 | 4340 | 8620 | 8740 | FeSi3 | FN02 | FN08 | FN0205 | M2 | P.A.N.A.C.E.A. | |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Chemical Compositions | C (%) | ≤ 0.07 | 0.35 – 0.45 | 0.14 – 0.19 | 0.80 – 1.05 | 0.20 – 0.50 | ≤ 0.06 | ≤ 0.60 | 0.35 – 0.50 | ≤ 0.15 | 0.4 – 0.6 | 0.35 – 0.45 | 0.12 – 0.23 | 0.45 – 0.55 | ≤ 0.10 | ≤ 0.10 | 0.4 – 0.6 | 0.4 – 0.6 | 0.95 – 1.05 | ≤ 0.2 |
Cr (%) | 15 –17.5 | 0.90 – 1.20 | 0.80 – 0.11 | 1.35 – 1.65 | 24 – 26 | 17 – 20 | 16 – 18 | 12 – 14 | - | - | 0.60 – 0.90 | 0.40 – 0.60 | 0.40 – 0.60 | - | - | - | - | 3.80 – 4.50 | 16.5 – 17.5 | |
Ni (%) | 3 – 5 | - | - | - | 19 – 22 | 8 – 11 | 10 – 14 | ≤ 0.60 | - | 1.5 – 2.5 | 1.65 – 2.00 | 0.40 – 0.70 | 0.50 – 0.80 | - | 1.9 – 2.2 | 7.5 – 8.5 | 1.9 – 2.2 | - | - | |
Cu (%) | 3 – 5 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |
Nb (%) | 0.15 – 0.45 | - | - | - | 1.2 – 1.5 | - | - | 1.0 – 2.0 | - | - | - | - | - | - | - | - | - | - | - | |
Mn (%) | ≤ 1 | - | 0.10 – 1.30 | - | ≤ 1.5 | ≤ 2 | ≤ 2 | ≤ 1.0 | 0.3 – 0.66 | - | - | - | - | - | - | - | - | - | 10 – 12 | |
Si (%) | ≤ 1 | - | < 0.50 | - | 0.75 – 1.30 | ≤ 1 | ≤ 1 | ≤ 1.0 | ≤ 0.4 | ≤ 1.0 | - | - | - | 2.5 – 3.0 | - | - | - | - | ≤ 1 | |
Mo (%) | - | 0.15 – 0.30 | - | - | - | - | 2 – 3 | ≤ 0.65 | - | 0.2 – 0.5 | 0.2 – 0.3 | 0.15 – 0.25 | 0.25 – 0.40 | - | - | - | - | 4.50 – 5.50 | 3.0 – 3.5 | |
P (%) | - | - | < 0.035 | - | - | - | - | ≤ 0.040 | ≤ 0.045 | - | - | - | - | - | - | - | - | - | - | |
S (%) | - | - | < 0.035 | - | - | - | - | ≤ 0.030 | ≤ 0.045 | - | - | - | - | - | - | - | - | - | - | |
N (%) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | 0.75 – 0.90 | |
W (%) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | 5.50 – 6.75 | - | |
V (%) | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | 1.75 – 2.20 | - | |
Other (%) | - | - | - | - | ≤ 2.0 | - | - | - | - | - | - | - | - | - | - | - | - | - | - | |
Fe (%) | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | Balance | |
Density | ≥ 7.55 g/cm3 | ≥ 7.40 g/cm3 | ≥ 7.40 g/cm3 | 7.50 g/cm3 | ≥ 7.60 g/cm3 | ≥ 7.7 g/cm3 | ≥ 7.8 g/cm3 | ≥ 7.55 g/cm3 | ≥7.5 g/cm3 | ≥ 7.5 g/cm3 | ≥ 7.50 g/cm3 | ≥ 7.4 g/cm3 | ≥ 7.5 g/cm3 | ≥ 7.5 g/cm3 | ≥ 7.5 g/cm3 | ≥ 7.5 g/cm3 | ≥ 7.5 g/cm3 | ≥ 7.8 g/cm3 | ≥ 7.5 g/cm3 | |
Yield Strength(YS) | As Sintered | 700 Mpa | ≥ 370 Mpa | ≥ 270 Mpa | ≥ 450 Mpa | ≥ 410 MPa | ≥ 140 MPa | ≥ 160 Mpa | ≥ 590 Mpa | ≥ 190 Mpa | ≥ 360 Mpa | ≥ 450 Mpa | ≥ 360 Mpa | ≥ 480 Mpa | ≥ 300 Mpa | ≥ 120 Mpa | ≥ 370 Mpa | ≥ 150 Mpa | ≥ 750 Mpa | ≥ 630 Mpa |
Heat Treated | ≥ 900 Mpa | ≥ 1190 MPa | ≥ 560 Mpa | - | - | - | - | - | - | 1030 Mpa | ≥ 1190 Mpa | - | ≥ 1320 MPa | - | - | ≥ 1050 Mpa | ≥ 660 MPa | - | - | |
Ultimate Tensile Strength(UTS) | As Sintered | 910 Mpa | ≥ 610 Mpa | ≥ 350 MPa | ≥ 840 Mpa | 750 Mpa | ≥ 560 Mpa | ≥ 450 Mpa | ≥ 740 MPa | ≥ 360 Mpa | ≥ 550 Mpa | ≥ 630 MPa | ≥ 610 Mpa | ≥ 800 Mpa | ≥ 500 Mpa | ≥ 230 Mpa | ≥ 650 Mpa | ≥ 340 Mpa | ≥ 1140 Mpa | ≥ 1030 Mpa |
Heat Treated | ≥ 1050 Mpa | ≥ 1380 MPa | ≥ 1010 Mpa | - | - | - | - | ≥ 1480 Mpa | - | 1240 Mpa | ≥ 1400 Mpa | - | ≥ 1520 MPa | - | - | ≥ 1180 MPa | ≥ 760 MPa | - | - | |
Elongation | As Sintered | 6% | ≥ 3 % | 15 % | ≥ 5 % | 16 % | ≥ 60 % | ≥ 50 % | ≥ 0.97 % | ≥ 26 % | ≥ 5 % | ≥ 7 % | ≥ 3 % | ≥ 8 % | ≥ 20 % | ≥ 25 % | ≥ 3 % | ≥ 3 % | ≥ 1 % | ≥ 35 % |
Heat Treated | ≥ 5 % | ≥ 2 % | 8 % | - | - | - | - | ≥ 0.85 % | - | ≥ 5 % | ≥ 2 % | - | ≥ 5 % | - | - | ≥ 3 % | ≥ 5 % | - | - | |
Hardness | As Sintered | ≤ 32 HRC | 100 – 230 HV10 | ≥ 110 HV | 180 – 290 HV10 | 210 HV1 | 130 HV10 | 110 HV10 | ≥ 560 HV1 | - | ≥ 120 HV10 | 170 – 250 HV10 | 150–230 HV10 | 140–210 HV10 | 120–160 HV1 | 70–110 HV10 | 130–280 HV10 | 100–150 HV10 | ≥ 48 HRC | 220–300 HV10 |
Heat Treated | ≥ 37 HRC | ≥ 40 HRC | ≥ 36 HRC | ≥ 55 HRC | - | - | - | ≥ 680 HV1 | 630 HV1 | ≥ 40 HRC | ≥ 42 HRC | ≥ 575 HV1 | ≥ 460 HV1 | - | ≥ 49 HRC | ≥ 38 HRC | 300 HV10 | ≥ 58 HRC | - | |
DIN Equivalent | 1.4542 | 1.7225 | 1.7131 | 1.3505 | 1.4848 | 1.4301 | 1.4404 | 1.4028 | - | - | 1.6565/1.6944, 40NiCrMo6 | 1.6523 | 1.6546 | 1.0884 | - | - | - | 1.3342 | - | |
AISI Equivalent | S17400 | 4140 | 16MoCr5 | E52100 | - | 304 | 316L | 420F | 1010 | - | 4340 | 8620 | 8740 | - | - | - | - | M2 (high C) | - |